[Properties]
High bond strength, rapid curing, not flow on vertical surface.
[Application]
It is widely used to bond wear resistant ceramic liner with metal, such as coal conveying system of thermal power plant, hopper and silo of discharging system etc.
Availability: | |
---|---|
Quantity: | |
[Properties]
High bond strength, rapid curing, not flow on vertical surface.
[Application]
It is widely used to bond wear resistant ceramic liner with metal, such as coal conveying system of thermal power plant, hopper and silo of discharging system etc.
[Chemical composition and physical properties]
Series | T1041 | T1011 | T1141 |
Color | White | White(light yellow) | White/Grey |
Density(g/cm3) | 1.28 | 1.66-1.70 | 1.48-1.52 |
Weight Ratio(A:B) | 4:1 | 1:1 | 4:1 |
Volume ratio(A:B) | 4:1 | 1:1 | 4:1 |
Operation time (200g mixing, min) | 30 | 30 | 30 |
Full curing time(h) | 24 | 24 | 24 |
Tensile strength (Mpa) GB/T6329-1996 | 65.0 | 65.0 | 35.0 |
Shear strength (Mpa) GB/T7124-2008 | ≥10 | ≥10 | ≥18 |
Working temperature(℃) | -60-150 | -60-150 | -60-200 |
Expiration date(years) | 2 | 2 | 2 |
Series | T8229 |
Color | Brown |
Density(g/cm3) | 2.25 |
Weight Ratio(A:B) | 2:1 |
Volume ratio(A:B) | 2:1 |
Operation time (200g mixing, min) | 30 |
Full curing time(h) | 24 |
After curing hardness (ShoreD)GB/T2411-2008 | 89.0 |
Compressive strength (Mpa)GB/T1041-2008 | 110.0 |
Tensile strength (Mpa)GB/T6329-1996 | 28.0 |
Shear strength (Mpa)GB/T7124-2008 | 16 |
Working temperature(℃) | -60-120 |
[Properties]
High bond strength, rapid curing, not flow on vertical surface.
[Application]
It is widely used to bond wear resistant ceramic liner with metal, such as coal conveying system of thermal power plant, hopper and silo of discharging system etc.
[Chemical composition and physical properties]
Series | T1041 | T1011 | T1141 |
Color | White | White(light yellow) | White/Grey |
Density(g/cm3) | 1.28 | 1.66-1.70 | 1.48-1.52 |
Weight Ratio(A:B) | 4:1 | 1:1 | 4:1 |
Volume ratio(A:B) | 4:1 | 1:1 | 4:1 |
Operation time (200g mixing, min) | 30 | 30 | 30 |
Full curing time(h) | 24 | 24 | 24 |
Tensile strength (Mpa) GB/T6329-1996 | 65.0 | 65.0 | 35.0 |
Shear strength (Mpa) GB/T7124-2008 | ≥10 | ≥10 | ≥18 |
Working temperature(℃) | -60-150 | -60-150 | -60-200 |
Expiration date(years) | 2 | 2 | 2 |
Series | T8229 |
Color | Brown |
Density(g/cm3) | 2.25 |
Weight Ratio(A:B) | 2:1 |
Volume ratio(A:B) | 2:1 |
Operation time (200g mixing, min) | 30 |
Full curing time(h) | 24 |
After curing hardness (ShoreD)GB/T2411-2008 | 89.0 |
Compressive strength (Mpa)GB/T1041-2008 | 110.0 |
Tensile strength (Mpa)GB/T6329-1996 | 28.0 |
Shear strength (Mpa)GB/T7124-2008 | 16 |
Working temperature(℃) | -60-120 |