[Properties]
1. High hardness, corrosion resistance, good chemical stability, can withstand the impact of high concentration and large particle materials for a long time.
2. Mohs hardness is 9.0, which is equivalent to HRC90 or above. It has high wear resistance for grinding medium in metallurgy, electric power, mining and coal industry, and its service life is dozens of times that quenched steel.
3. The inner surface is smooth without convex helix, the resistance coefficient is 0.0193, and the inner surface glossy degree is better than any metal pipe.
4. No rust on inner surface.
[Application]
It is used for material conveying equipment in electric power, metallurgy, coal, petroleum, cement, chemical industry and machinery industry etc.
Availability: | |
---|---|
Quantity: | |
[Properties]
1. High hardness, corrosion resistance, good chemical stability, can withstand the impact of high concentration and large particle materials for a long time.
2. Mohs hardness is 9.0, which is equivalent to HRC90 or above. It has high wear resistance for grinding medium in metallurgy, electric power, mining and coal industry, and its service life is dozens of times that quenched steel.
3. The inner surface is smooth without convex helix, the resistance coefficient is 0.0193, and the inner surface glossy degree is better than any metal pipe.
4. No rust on inner surface.
[Application]
It is used for material conveying equipment in electric power, metallurgy, coal, petroleum, cement, chemical industry and machinery industry etc.
[Chemical Composition and Physical Properties]
Series | T36H | TG365H | TE37H | T377H | ZTA |
AL2O3(%) | 92±0.5 | 95±0.5 | 95±0.5 | ≥96 | ≥75 |
Bulk density(g/cm3) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.77 | ≥4.1 |
Bending strength (Mpa) | ≥220 | ≥250 | ≥300 | ≥300 | ≥400 |
Compressive Strength (Mpa) | ≥1050 | ≥1300 | ≥1600 | ≥1700 | ≥2000 |
Fracture Toughness (MPam1/2) | ≥3.7 | ≥3.8 | ≥4.0 | ≥4.1 | ≥4.5 |
Rockwell hardness (HRA) | ≥82 | ≥85 | ≥88 | ≥90 | ≥90 |
Hardness (Mohs) | 9 | 9 | 9 | 9 | 9 |
[Properties]
1. High hardness, corrosion resistance, good chemical stability, can withstand the impact of high concentration and large particle materials for a long time.
2. Mohs hardness is 9.0, which is equivalent to HRC90 or above. It has high wear resistance for grinding medium in metallurgy, electric power, mining and coal industry, and its service life is dozens of times that quenched steel.
3. The inner surface is smooth without convex helix, the resistance coefficient is 0.0193, and the inner surface glossy degree is better than any metal pipe.
4. No rust on inner surface.
[Application]
It is used for material conveying equipment in electric power, metallurgy, coal, petroleum, cement, chemical industry and machinery industry etc.
[Chemical Composition and Physical Properties]
Series | T36H | TG365H | TE37H | T377H | ZTA |
AL2O3(%) | 92±0.5 | 95±0.5 | 95±0.5 | ≥96 | ≥75 |
Bulk density(g/cm3) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.77 | ≥4.1 |
Bending strength (Mpa) | ≥220 | ≥250 | ≥300 | ≥300 | ≥400 |
Compressive Strength (Mpa) | ≥1050 | ≥1300 | ≥1600 | ≥1700 | ≥2000 |
Fracture Toughness (MPam1/2) | ≥3.7 | ≥3.8 | ≥4.0 | ≥4.1 | ≥4.5 |
Rockwell hardness (HRA) | ≥82 | ≥85 | ≥88 | ≥90 | ≥90 |
Hardness (Mohs) | 9 | 9 | 9 | 9 | 9 |